RTP Company RTP 2100 TFE 40 Polyetherimide (PEI), PTFE Lubricated

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2100 TFE 40 Polyetherimide (PEI), PTFE Lubricated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.53 g/cc
1.53 g/cc
ASTM D 792
Linear Mold Shrinkage 0.0060 - 0.010 cm/cm

@Thickness 3.17 mm
0.0060 - 0.010 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 54.1 MPa
7850 psi
ASTM D 638
Elongation at Break 5.0 - 8.0 %
5.0 - 8.0 %
ASTM D 638
Tensile Modulus 2.14 GPa
310 ksi
ASTM D 638
Flexural Strength 80.0 MPa
11600 psi
ASTM D 790
Flexural Modulus 2.21 GPa
320 ksi
ASTM D 790
Izod Impact, Notched 0.427 J/cm

@Thickness 3.17 mm
0.800 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 4.27 J/cm

@Thickness 3.17 mm
8.00 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
ASTM D 257
Surface Resistivity per Square >= 1.00e+14 ohm
>= 1.00e+14 ohm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 354 - 399 °C
670 - 750 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C
300 °F
Dry Time 4 hour
4 hour
Moisture Content 0.040 %
0.040 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 82.7 - 124 MPa
12000 - 18000 psi