Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.27 g/cc
1.27 g/cc
ASTM D 792
Water Absorption 0.25 %

@Time 86400 sec
0.25 %

@Time 24.0 hour
ASTM D 570
Linear Mold Shrinkage 0.0080 cm/cm

@Thickness 3.17 mm
0.0080 in/in

@Thickness 0.125 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 109 MPa
15800 psi
ASTM D 638
Elongation at Break 6.0 - 10 %
6.0 - 10 %
ASTM D 638
Tensile Modulus 3.31 GPa
480 ksi
ASTM D 638
Flexural Strength 145 MPa
21000 psi
ASTM D 790
Flexural Modulus 3.31 GPa
480 ksi
ASTM D 790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.17 mm
1.00 ft-lb/in

@Thickness 0.125 in
ASTM D 256
Izod Impact, Unnotched 13.3 J/cm

@Thickness 3.17 mm
25.0 ft-lb/in

@Thickness 0.125 in
ASTM D 4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.8 µm/m-°C
31.0 µin/in-°F
ASTM E 831
Thermal Conductivity 0.216 W/m-K
1.50 BTU-in/hr-ft²-°F
Through-plane; ASTM E 1530
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+12 ohm-cm
>= 1.00e+12 ohm-cm
ASTM D 257
Dielectric Constant 3.2

@Frequency 1.00e+6 Hz
3.2

@Frequency 1.00e+6 Hz
Dry; ASTM D 150
Dielectric Strength 19.7 kV/mm
500 kV/in
short term, in oil; ASTM D 149
Dissipation Factor 0.0040

@Frequency 1.00e+6 Hz
0.0040

@Frequency 1.00e+6 Hz
Dry; ASTM D 150
Processing Properties Metric English Comments
Melt Temperature 354 - 399 °C
670 - 750 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C

@Time 14400 sec
300 °F

@Time 4.00 hour
Moisture Content 0.040 %
0.040 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 82.7 - 124 MPa
12000 - 18000 psi