RTP Company RTP 2099 X 134514 Polycarbonate/Polyester Flame Retardant - UV Stabilized - Chemical Resistant Alloy

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2099 X 134514 Polycarbonate/Polyester Flame Retardant - UV Stabilized - Chemical Resistant Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.28 g/cc
1.28 g/cc
ASTM D 792
Linear Mold Shrinkage 0.00600 - 0.00900 cm/cm

@Thickness 3.20 mm
0.00600 - 0.00900 in/in

@Thickness 0.126 in
ASTM D 955
Melt Flow 35.0 g/10 min

@Load 10.0 kg,
Temperature 250 °C
35.0 g/10 min

@Load 22.0 lb,
Temperature 482 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.5 MPa
9500 psi
ASTM D 638
Elongation at Break >= 10.0 %
>= 10.0 %
ASTM D 638
Tensile Modulus 2.41 GPa
350 ksi
ASTM D 638
Flexural Strength 107 MPa
15500 psi
ASTM D 790
Flexural Modulus 2.76 GPa
400 ksi
ASTM D 790
Izod Impact, Notched 6.41 J/cm

@Thickness 3.20 mm
12.0 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched NB

@Thickness 3.20 mm
NB

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
5VA

@Thickness 2.00 mm
5VA

@Thickness 0.0787 in
Processing Properties Metric English Comments
Melt Temperature 243 - 271 °C
470 - 520 °F
Mold Temperature 60.0 - 93.3 °C
140 - 200 °F
Drying Temperature 82.2 - 104 °C

@Time 14400 sec
180 - 220 °F

@Time 4.00 hour
Moisture Content <= 0.0200 %
<= 0.0200 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi