RTP Company RTP 2099 X 131060 A Bio-Based Polylactic Acid (PLA), PLA ALLOY - Flame Retardant - Halogen Free - 20% Renewable Resource Content - Additional 45% Post Consumer Content

Category Polymer , Renewable/Recycled Polymer , Thermoplastic
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2099 X 131060 A Bio-Based Polylactic Acid (PLA), PLA ALLOY - Flame Retardant - Halogen Free - 20% Renewable Resource Content - Additional 45% Post Consumer Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.31 g/cc
1.31 g/cc
ASTM D 792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm

@Thickness 3.17 mm
0.0050 - 0.0070 in/in

@Thickness 0.125 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.3 MPa
7000 psi
ASTM D 638
Elongation at Break >= 10 %
>= 10 %
ASTM D 638
Tensile Modulus 3.79 GPa
550 ksi
ASTM D 638
Flexural Strength 86.2 MPa
12500 psi
ASTM D 790
Flexural Modulus 3.79 GPa
550 ksi
ASTM D 790
Izod Impact, Notched 1.33 J/cm

@Thickness 3.17 mm
2.50 ft-lb/in

@Thickness 0.125 in
ASTM D 256
Izod Impact, Unnotched NB

@Thickness 3.17 mm
NB

@Thickness 0.125 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 96.1 °C
205 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Processing Properties Metric English Comments
Melt Temperature 193 - 210 °C
380 - 410 °F
Mold Temperature 0.000 - 26.7 °C
32.0 - 80.0 °F
Drying Temperature 60.0 °C

@Time 14400 - 21600 sec
140 °F

@Time 4.00 - 6.00 hour
Moisture Content <= 0.020 %
<= 0.020 %
Injection Pressure 55.2 - 103 MPa
8000 - 15000 psi