RTP Company RTP 2099 X 126218 C Bio-Based Polylactic Acid (PLA); Impact Modified - 84% Renewable Resource Content

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2099 X 126218 C Bio-Based Polylactic Acid (PLA); Impact Modified - 84% Renewable Resource Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
For detailed processing information, see the PLA Molding Guide on the RTP Company website.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.1 MPa
6400 psi
ASTM D 638
Elongation at Break >= 10 %
>= 10 %
ASTM D 638
Tensile Modulus 2.62 GPa
380 ksi
ASTM D 638
Flexural Strength 68.9 MPa
10000 psi
ASTM D 790
Flexural Modulus 2.69 GPa
390 ksi
ASTM D 790
Izod Impact, Notched 1.87 J/cm

@Thickness 3.20 mm
3.50 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched NB

@Thickness 3.20 mm
NB

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 51.1 °C
124 °F
ASTM D 648
Processing Properties Metric English Comments
Melt Temperature 171 - 188 °C
340 - 370 °F
Mold Temperature 10.0 - 23.9 °C
50.0 - 75.0 °F
Drying Temperature 48.9 °C

@Time 7200 - 21600 sec
120 °F

@Time 2.00 - 6.00 hour
Moisture Content 0.020 %
0.020 %
Dew Point -40.0 °C
-40.0 °F
Injection Pressure 55.2 - 103 MPa
8000 - 15000 psi