RTP Company RTP 2099 X 124789 D Bio-Based Polylactic Acid (PLA); Impact Modified - Transparent - 79%Renewable Resource Content

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2099 X 124789 D Bio-Based Polylactic Acid (PLA); Impact Modified - Transparent - 79%Renewable Resource Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Not optically transparent.  Thick wall sections can be hazy. For detailed processing information, see the PLA Molding Guide on the RTP Company website.
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
ASTM D 792
Mechanical Properties Metric English Comments
Tensile Strength at Break 41.4 MPa
6000 psi
ASTM D 638
Elongation at Break >= 10 %
>= 10 %
ASTM D 638
Tensile Modulus 2.55 GPa
370 ksi
ASTM D 638
Flexural Strength 62.1 MPa
9000 psi
ASTM D 790
Flexural Modulus 2.55 GPa
370 ksi
ASTM D 790
Izod Impact, Notched 2.67 J/cm

@Thickness 3.20 mm
5.00 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched NB

@Thickness 3.20 mm
NB

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 51.1 °C
124 °F
ASTM D 648
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Processing Properties Metric English Comments
Melt Temperature 171 - 188 °C
340 - 370 °F
Mold Temperature 10.0 - 23.9 °C
50.0 - 75.0 °F
Drying Temperature 48.9 °C

@Time 7200 - 21600 sec
120 °F

@Time 2.00 - 6.00 hour
Moisture Content 0.020 %
0.020 %
Dew Point -40.0 °C
-40.0 °F
Injection Pressure 55.2 - 103 MPa
8000 - 15000 psi