- RTP Company RTP 2099 X 121249 C Bio-Based Polylactic Acid (PLA); Standard Nucleator - Glass Fiber - 68% Renewable Resource Content
RTP Company RTP 2099 X 121249 C Bio-Based Polylactic Acid (PLA); Standard Nucleator - Glass Fiber - 68% Renewable Resource Content
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer |
| Manufacturer | RTP Company |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RTP Company RTP 2099 X 121249 C Bio-Based Polylactic Acid (PLA); Standard Nucleator - Glass Fiber - 68% Renewable Resource Content.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nucleated for high heat exposure. For detailed processing information regarding this, see the PLA Molding Guide on the RTP Company website. This material has received the "USDA Certified Biobased Product" label through the BioPreferred program with 99% biobased carbon content per ASTM 6866.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ASTM D 792 |
| Additive Loading | 30 % | 30 % | Primary Additive |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 110 MPa | 16000 psi | ASTM D 638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D 638 |
| Tensile Modulus | 10.2 GPa | 1480 ksi | ASTM D 638 |
| Flexural Strength | 145 MPa | 21000 psi | ASTM D 790 |
| Flexural Modulus | 11.2 GPa | 1630 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.534 J/cm @Thickness 3.20 mm |
1.00 ft-lb/in @Thickness 0.126 in |
ASTM D 256 |
| Izod Impact, Unnotched | 3.20 J/cm @Thickness 3.20 mm |
6.00 ft-lb/in @Thickness 0.126 in |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D 648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 171 - 193 °C | 340 - 380 °F | |
| Mold Temperature | 82.2 - 104 °C | 180 - 220 °F | |
| Drying Temperature | 54.4 °C @Time 7200 - 21600 sec |
130 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | 0.020 % | 0.020 % | |
| Dew Point | -40.0 °C | -40.0 °F | |
| Injection Pressure | 55.2 - 103 MPa | 8000 - 15000 psi |