RTP Company RTP 2099 X 121249 A Bio-Based Polylactic Acid (PLA); Standard Nucleator - Glass Fiber - 88% Renewable Resource Content

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2099 X 121249 A Bio-Based Polylactic Acid (PLA); Standard Nucleator - Glass Fiber - 88% Renewable Resource Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Nucleated for high heat exposure.  For detailed processing information regarding this, see the PLA Molding Guide on the RTP Company website.
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D 792
Additive Loading 10 %
10 %
Primary Additive
Mechanical Properties Metric English Comments
Tensile Strength at Break 79.3 MPa
11500 psi
ASTM D 638
Elongation at Break 1.5 %
1.5 %
ASTM D 638
Tensile Modulus 6.89 GPa
1000 ksi
ASTM D 638
Flexural Strength 93.1 MPa
13500 psi
ASTM D 790
Flexural Modulus 6.55 GPa
950 ksi
ASTM D 790
Izod Impact, Notched 0.427 J/cm

@Thickness 3.20 mm
0.800 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 3.20 J/cm

@Thickness 3.20 mm
6.00 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 143 °C
290 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 106 °C
222 °F
ASTM D 648
Processing Properties Metric English Comments
Melt Temperature 171 - 193 °C
340 - 380 °F
Mold Temperature 82.2 - 104 °C
180 - 220 °F
Drying Temperature 54.4 °C

@Time 7200 - 21600 sec
130 °F

@Time 2.00 - 6.00 hour
Moisture Content 0.020 %
0.020 %
Dew Point -40.0 °C
-40.0 °F
Injection Pressure 55.2 - 103 MPa
8000 - 15000 psi