RTP Company RTP 2099 X 121235 D Bio-Based Polylactic Acid (PLA); PC-PLA Blend - 31% Renewable Resource Content

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2099 X 121235 D Bio-Based Polylactic Acid (PLA); PC-PLA Blend - 31% Renewable Resource Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
For detailed processing information, see the PLA Molding Guide on the RTP Company website.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D 792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.3 MPa
7000 psi
ASTM D 638
Elongation at Break >= 10 %
>= 10 %
ASTM D 638
Tensile Modulus 2.07 GPa
300 ksi
ASTM D 638
Flexural Strength 82.7 MPa
12000 psi
ASTM D 790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D 790
Izod Impact, Notched 8.54 J/cm

@Thickness 3.20 mm
16.0 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched NB

@Thickness 3.20 mm
NB

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 116 °C
240 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 54.4 °C
130 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Processing Properties Metric English Comments
Melt Temperature 221 - 243 °C
430 - 470 °F
Mold Temperature 23.9 - 71.1 °C
75.0 - 160 °F
Drying Temperature 79.4 °C

@Time 14400 sec
175 °F

@Time 4.00 hour
Moisture Content 0.020 %
0.020 %
Dew Point -40.0 °C
-40.0 °F
Injection Pressure 55.2 - 103 MPa
8000 - 15000 psi