RTP Company RTP 2099 X 115387 A Biobased Polyamide (PA) Glass Fiber - 43% Bio-Content

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2099 X 115387 A Biobased Polyamide (PA) Glass Fiber - 43% Bio-Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.30 g/cc
1.30 g/cc
ASTM D 792
Water Absorption 0.25 %

@Temperature 23.0 °C,
Time 86400 sec
0.25 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D 570
Linear Mold Shrinkage 0.0030 cm/cm

@Thickness 3.20 mm
0.0030 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 138 MPa
20000 psi
ASTM D 638
Elongation at Break 5.0 %
5.0 %
ASTM D 638
Flexural Strength 207 MPa
30000 psi
ASTM D 790
Flexural Modulus 7.93 GPa
1150 ksi
ASTM D 790
Izod Impact, Notched 1.60 J/cm

@Thickness 3.20 mm
3.00 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 13.3 J/cm

@Thickness 3.20 mm
25.0 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 216 °C
420 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 204 °C
400 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Processing Properties Metric English Comments
Melt Temperature 232 - 260 °C
450 - 500 °F
Mold Temperature 51.7 - 79.4 °C
125 - 175 °F
Drying Temperature 79.4 °C

@Time 7200 sec
175 °F

@Time 2.00 hour
Moisture Content 0.20 %
0.20 %
Dew Point -17.8 °C
0.000 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi