RTP Company RTP 205.3 FR Nylon 6/6 (PA) Glass Fiber - Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 205.3 FR Nylon 6/6 (PA) Glass Fiber - Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.69 g/cc
1.69 g/cc
ASTM D 792
Water Absorption 0.60 %

@Temperature 23.0 °C,
Time 86400 sec
0.60 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D 570
Additive Loading 33 %
33 %
Primary Additive
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0020 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 159 MPa
23000 psi
ASTM D 638
Elongation at Break 2.0 - 3.0 %
2.0 - 3.0 %
ASTM D 638
Tensile Modulus 13.1 GPa
1900 ksi
ASTM D 638
Flexural Strength 241 MPa
35000 psi
ASTM D 790
Flexural Modulus 11.4 GPa
1650 ksi
ASTM D 790
Izod Impact, Notched 0.908 J/cm

@Thickness 3.20 mm
1.70 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 8.01 J/cm

@Thickness 3.20 mm
15.0 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 249 °C
480 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 232 °C
450 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Processing Properties Metric English Comments
Melt Temperature 277 - 299 °C
530 - 570 °F
Mold Temperature 65.6 - 107 °C
150 - 225 °F
Drying Temperature 79.4 °C

@Time 14400 sec
175 °F

@Time 4.00 hour
Moisture Content 0.20 %
0.20 %
Dew Point -17.8 °C
0.000 °F
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi