RTP Company RTP 205 C Nylon 11 (PA); Glass Fiber - 68% Renewable Resource Content

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11 with 30% Glass Fiber Filler
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 205 C Nylon 11 (PA); Glass Fiber - 68% Renewable Resource Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Renewable Resource Content calculated based on % of total compound weight.
Physical Properties Metric English Comments
Specific Gravity 1.25 g/cc
1.25 g/cc
ASTM D 792
Additive Loading 30 %
30 %
Primary Additive
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 86.2 MPa
12500 psi
ASTM D 638
Elongation at Break 2.5 - 3.5 %
2.5 - 3.5 %
ASTM D 638
Tensile Modulus 6.55 GPa
950 ksi
ASTM D 638
Flexural Strength 124 MPa
18000 psi
ASTM D 790
Flexural Modulus 5.52 GPa
800 ksi
ASTM D 790
Izod Impact, Notched 1.07 J/cm

@Thickness 3.20 mm
2.00 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 5.87 J/cm

@Thickness 3.20 mm
11.0 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Processing Properties Metric English Comments
Melt Temperature 224 - 288 °C
435 - 550 °F
Mold Temperature 37.8 - 65.6 °C
100 - 150 °F
Drying Temperature 79.4 °C

@Time 14400 sec
175 °F

@Time 4.00 hour
Moisture Content 0.20 %
0.20 %
Dew Point -17.8 °C
0.000 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi