RTP Company RTP 205 A TFE 13 SI 2 Nylon 6 (PA), Glass Fiber - PTFE Lubricated - Silicone Lubricated

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber/Solid Lube Filled
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 205 A TFE 13 SI 2 Nylon 6 (PA), Glass Fiber - PTFE Lubricated - Silicone Lubricated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ASTM D 792
Filler Content 30 %
30 %
Primary Additive
Linear Mold Shrinkage 0.0010 - 0.0040 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0040 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 128 MPa
18500 psi
ASTM D 638
Elongation at Break 3.0 - 4.5 %
3.0 - 4.5 %
ASTM D 638
Tensile Modulus 8.96 GPa
1300 ksi
ASTM D 638
Flexural Strength 193 MPa
28000 psi
ASTM D 790
Flexural Modulus 7.93 GPa
1150 ksi
ASTM D 790
Izod Impact, Notched 1.39 J/cm

@Thickness 3.17 mm
2.60 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 12.0 J/cm

@Thickness 3.17 mm
22.5 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 199 °C
390 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Processing Properties Metric English Comments
Melt Temperature 243 - 279 °C
470 - 535 °F
Mold Temperature 54.4 - 93.3 °C
130 - 200 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 2 hour
2 hour
Moisture Content 0.20 %
0.20 %
Dew Point -17.8 °C
0.000 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi