RTP Company RTP 205 A FR Nylon 6 (PA), Glass Fiber - Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Glass Fiber Filled, Flame Retardant
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 205 A FR Nylon 6 (PA), Glass Fiber - Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.65 g/cc
1.65 g/cc
ASTM D 792
Water Absorption 1.2 %

@Time 86400 sec
1.2 %

@Time 24.0 hour
ASTM D 570
Additive Loading 30 %
30 %
Primary Additive
Linear Mold Shrinkage 0.0015 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0015 - 0.0030 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 119
119
ASTM D 785
Tensile Strength at Break 155 MPa
22500 psi
ASTM D 638
Elongation at Break 2.8 %
2.8 %
ASTM D 638
Tensile Modulus 12.4 GPa
1800 ksi
ASTM D 638
Flexural Strength 241 MPa
35000 psi
ASTM D 790
Flexural Modulus 10.3 GPa
1500 ksi
ASTM D 790
Izod Impact, Notched 1.33 J/cm

@Thickness 3.20 mm
2.50 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 9.61 J/cm

@Thickness 3.20 mm
18.0 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 216 °C
420 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 199 °C
390 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
5VA

@Thickness 3.00 mm
5VA

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
ASTM D 257
Dielectric Constant 4.2

@Frequency 1.00e+6 Hz
4.2

@Frequency 1.00e+6 Hz
Dry; ASTM D 150
Dielectric Strength 18.7 kV/mm
475 kV/in
in oil; ASTM D 149
Dissipation Factor 0.013

@Frequency 1.00e+6 Hz
0.013

@Frequency 1.00e+6 Hz
Dry; ASTM D 150
Processing Properties Metric English Comments
Melt Temperature 243 - 279 °C
470 - 535 °F
Mold Temperature 54.4 - 93.3 °C
130 - 200 °F
Drying Temperature 82.2 °C

@Time 7200 sec
180 °F

@Time 2.00 hour
Moisture Content 0.20 %
0.20 %
Dew Point -17.8 °C
0.000 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi