- RTP Company RTP 200 D UV Nylon 6/12 (PA); UV Stabilized
RTP Company RTP 200 D UV Nylon 6/12 (PA); UV Stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Unreinforced |
| Manufacturer | RTP Company |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RTP Company RTP 200 D UV Nylon 6/12 (PA); UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM D 792 |
| Linear Mold Shrinkage | 0.018 - 0.025 cm/cm @Thickness 3.20 mm |
0.018 - 0.025 in/in @Thickness 0.126 in |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.1 MPa | 9000 psi | ASTM D 638 |
| Elongation at Break | >= 10 % | >= 10 % | ASTM D 638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | ASTM D 638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D 790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D 790 |
| Izod Impact, Notched | 0.374 J/cm @Thickness 3.20 mm |
0.700 ft-lb/in @Thickness 0.126 in |
ASTM D 256 |
| Izod Impact, Unnotched | NB @Thickness 3.20 mm |
NB @Thickness 0.126 in |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 87.8 °C | 190 °F | ASTM D 648 |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 249 - 285 °C | 480 - 545 °F | |
| Mold Temperature | 60.0 - 93.3 °C | 140 - 200 °F | |
| Drying Temperature | 79.4 °C @Time 14400 sec |
175 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % | |
| Dew Point | -17.8 °C | 0.000 °F | |
| Injection Pressure | 68.9 - 124 MPa | 10000 - 18000 psi |
Users viewing this material also viewed the following:
- Nye Lubricants 723F6-EP (RL) Rheolube Grease
- RheTech Products RCT140-01A 40% Talc Reinforced Polypropylene, Black, Recycled Content
- SABIC Innovative Plastics Cycoloy® C1200HF PC+ABS (Asia Pacific)
- Celanese Celanex® 2302 GV1/15 PBT, 15% Glass Reinforced (Unverified Data**)
- RTP Company RTP 981 Polysulfone (PSU), Carbon Fiber
- Hyosung Topilene C600HF PP
- A. Schulman POLYBATCH™ Yellow 2600V Concentrate Based In Polyethylene
- Dow Corning SILASTIC® 25785-V SILICONE RUBBER RED
- Ineos Nova 5104 High Impact Polystyrene (discontinued **)
Copyright © lookpolymers.com All Rights Reserved