RTP Company RTP 200 C TFE 10 Nylon 11 (PA); PTFE Lubricated - 89% Renewable Resource Content

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 11 , Nylon 11 with PTFE Filler
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 200 C TFE 10 Nylon 11 (PA); PTFE Lubricated - 89% Renewable Resource Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Renewable Resource Content calculated based on % of total compound weight.
Physical Properties Metric English Comments
Specific Gravity 1.09 g/cc
1.09 g/cc
ASTM D 792
Linear Mold Shrinkage 0.015 - 0.025 cm/cm

@Thickness 3.20 mm
0.015 - 0.025 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 34.5 MPa
5000 psi
ASTM D 638
Elongation at Break >= 10 %
>= 10 %
ASTM D 638
Tensile Modulus 1.38 GPa
200 ksi
ASTM D 638
Flexural Strength 51.7 MPa
7500 psi
ASTM D 790
Flexural Modulus 1.38 GPa
200 ksi
ASTM D 790
Izod Impact, Notched 0.694 J/cm

@Thickness 3.20 mm
1.30 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched NB

@Thickness 3.20 mm
NB

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 54.4 °C
130 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Processing Properties Metric English Comments
Melt Temperature 224 - 288 °C
435 - 550 °F
Mold Temperature 37.8 - 65.6 °C
100 - 150 °F
Drying Temperature 79.4 °C

@Time 14400 sec
175 °F

@Time 4.00 hour
Moisture Content 0.20 %
0.20 %
Dew Point -17.8 °C
0.000 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi