- RTP Company RTP 199 X 137777 C Polypropylene (PP) Co-Polymer - High Flow - High Impact - Flame Retardant - UV Stabilized
RTP Company RTP 199 X 137777 C Polypropylene (PP) Co-Polymer - High Flow - High Impact - Flame Retardant - UV Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer |
| Manufacturer | RTP Company |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RTP Company RTP 199 X 137777 C Polypropylene (PP) Co-Polymer - High Flow - High Impact - Flame Retardant - UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 g/cc | 1.03 g/cc | ASTM D 792 |
| Linear Mold Shrinkage | 0.0150 - 0.0200 cm/cm @Thickness 3.20 mm |
0.0150 - 0.0200 in/in @Thickness 0.126 in |
ASTM D 955 |
| Melt Flow | 35.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
35.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 17.9 MPa | 2600 psi | ASTM D 638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D 638 |
| Tensile Modulus | 0.827 GPa | 120 ksi | ASTM D 638 |
| Flexural Strength | 26.2 MPa | 3800 psi | ASTM D 790 |
| Flexural Modulus | 0.827 GPa | 120 ksi | ASTM D 790 |
| Izod Impact, Notched | 6.41 J/cm @Thickness 3.20 mm |
12.0 ft-lb/in @Thickness 0.126 in |
ASTM D 256 |
| Izod Impact, Unnotched | NB @Thickness 3.20 mm |
NB @Thickness 0.126 in |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 191 - 232 °C | 375 - 450 °F | |
| Mold Temperature | 32.2 - 65.6 °C | 90.0 - 150 °F | |
| Drying Temperature | 79.4 °C @Time 7200 sec |
175 °F @Time 2.00 hour |
|
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi |
Users viewing this material also viewed the following:
- Nye Lubricants 717E(RL) Rheolube Grease
- Polimeri Europa Sinkral® B 532/E ABS Resin
- Polykemi AB POLYblend 45FS GKF2505 PC/ABS-Blend, Glass Fiber reinforced
- Indium Corp. Indalloy 104 Tin-Lead Solder Alloy
- Total 3802 B HDPE, cable, sheet, pipe, injection molding
- CIMBAR Miti-Wite B1 Chemically Purified White Barite (BaSO4)
- Elkem 20 02 Silicon 99 Refined
- Dow TUFLIN™ HS-7021 NT 7 Linear Low Density Polyethylene Resin
- Technetics Group Texolon™ 8534 PTFE (Unverified Data**)
- Celanese VECTRA S475 LCP, 32% Mineral / Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved