RTP Company RTP 199 X 125445 B Polypropylene (PP), Cellulose Fiber - 30% Renewable Resource Content - Additional 56% Post Consumer Recycled Content

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Wood Filled
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 199 X 125445 B Polypropylene (PP), Cellulose Fiber - 30% Renewable Resource Content - Additional 56% Post Consumer Recycled Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% renewable content based on % of total compound weight.
Physical Properties Metric English Comments
Specific Gravity 1.02 g/cc
1.02 g/cc
ASTM D 792
Linear Mold Shrinkage 0.0030 - 0.0060 cm/cm

@Thickness 3.17 mm
0.0030 - 0.0060 in/in

@Thickness 0.125 in
ASTM D 955
Melt Flow 0.50 g/10 min

@Load 2.16 kg,
Temperature 230 °C
0.50 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 41.4 MPa
6000 psi
ASTM D 638
Elongation at Break 4.0 - 6.0 %
4.0 - 6.0 %
ASTM D 638
Tensile Modulus 2.55 GPa
370 ksi
ASTM D 638
Flexural Strength 68.9 MPa
10000 psi
ASTM D 790
Flexural Modulus 2.76 GPa
400 ksi
ASTM D 790
Izod Impact, Notched 0.481 J/cm

@Thickness 3.17 mm
0.900 ft-lb/in

@Thickness 0.125 in
ASTM D 256
Izod Impact, Unnotched 3.20 J/cm

@Thickness 3.17 mm
6.00 ft-lb/in

@Thickness 0.125 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 119 °C
247 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 63.3 °C
146 °F
ASTM D 648
Processing Properties Metric English Comments
Melt Temperature 191 - 232 °C
375 - 450 °F
Mold Temperature 32.2 - 65.6 °C
90.0 - 150 °F
Drying Temperature 79.4 °C

@Time 7200 sec
175 °F

@Time 2.00 hour
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi