RTP Company RTP 199 X 124797 B Polypropylene (PP), Cellulose Fiber - 30% Renewable Resource Content

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Wood Filled
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 199 X 124797 B Polypropylene (PP), Cellulose Fiber - 30% Renewable Resource Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% renewable content based on % of total compound weight.
Physical Properties Metric English Comments
Specific Gravity 1.02 g/cc
1.02 g/cc
ASTM D 792
Linear Mold Shrinkage 0.0030 - 0.0060 cm/cm

@Thickness 3.17 mm
0.0030 - 0.0060 in/in

@Thickness 0.125 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 48.3 MPa
7000 psi
ASTM D 638
Elongation at Break 5.0 - 7.0 %
5.0 - 7.0 %
ASTM D 638
Tensile Modulus 2.76 GPa
400 ksi
ASTM D 638
Flexural Strength 68.9 MPa
10000 psi
ASTM D 790
Flexural Modulus 2.76 GPa
400 ksi
ASTM D 790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.17 mm
1.00 ft-lb/in

@Thickness 0.125 in
ASTM D 256
Izod Impact, Unnotched 4.54 J/cm

@Thickness 3.17 mm
8.50 ft-lb/in

@Thickness 0.125 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 142 °C
288 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 77.8 °C
172 °F
ASTM D 648
Processing Properties Metric English Comments
Melt Temperature 191 - 232 °C
375 - 450 °F
Mold Temperature 32.2 - 65.6 °C
90.0 - 150 °F
Drying Temperature 79.4 °C

@Time 7200 sec
175 °F

@Time 2.00 hour
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi