RTP Company RTP 1607 Polyarylsulfone (PAS), Glass Fiber 40%  (discontinued **)

Category Polymer , Thermoplastic , Polyarylsulfone (PAS) , Polyarylsulfone (PAS), Glass Fiber 40%
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 1607 Polyarylsulfone (PAS), Glass Fiber 40%  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data is for injection molded specimens and was provided by the manufacturer, RTP Company.This product has been discontinued, please contact RTP Company regarding alternate grades.
Physical Properties Metric English Comments
Density 1.68 g/cc
0.0607 lb/in³
ASTM D792
Water Absorption 0.28 %
0.28 %
24 hrs @ 23°C; ASTM D570
Linear Mold Shrinkage 0.0010 cm/cm

@Thickness 3.20 mm
0.0010 in/in

@Thickness 0.126 in
ASTM D955
0.0020 cm/cm

@Thickness 6.40 mm
0.0020 in/in

@Thickness 0.252 in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 155 MPa
22500 psi
ASTM D638
Elongation at Break 1.3 %
1.3 %
ASTM D638
Tensile Modulus 11.0 GPa
1600 ksi
ASTM D638
Flexural Yield Strength 214 MPa
31000 psi
ASTM D790
Flexural Modulus 10.3 GPa
1490 ksi
ASTM D790
Izod Impact, Notched 1.00 J/cm

@Thickness 3.20 mm
1.87 ft-lb/in

@Thickness 0.126 in
ASTM D256
Izod Impact, Unnotched 6.90 J/cm

@Thickness 3.20 mm
12.9 ft-lb/in

@Thickness 0.126 in
ASTM D256
K (wear) Factor 10100 x 10-8 mm³/N-M
5000 x 10-10 in³-min/ft-lb-hr
at 50 fpm, 2000 PV against C1018 Steel HRC 15-25, 14-17 microsmoothness; ASTM D 3702
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 216 °C
421 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 216 °C
421 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
Values per RTP Company Testing.; UL94
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Constant 4.3

@Frequency 1e+6 Hz
4.3

@Frequency 1e+6 Hz
Dry; ASTM D150
Dielectric Strength 16.0 kV/mm
406 kV/in
S/T; ASTM D149
Dissipation Factor 0.0080

@Frequency 1e+6 Hz
0.0080

@Frequency 1e+6 Hz
Dry; ASTM D150