RTP Company RTP 154 HI Polypropylene (PP), Copolymer - Flame Retardant

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 154 HI Polypropylene (PP), Copolymer - Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The RTP 154 family of compounds are flame retarded, unreinforced polypropylene materials. They offer improved physical properties, low specific gravity and excellent moldability vs. traditional V-0 polypropylenes.
Physical Properties Metric English Comments
Specific Gravity 1.03 g/cc
1.03 g/cc
ASTM D 792
Water Absorption 0.010 %
0.010 %
24 hrs @ 23°C; ASTM D 570
Linear Mold Shrinkage 0.015 - 0.020 cm/cm

@Thickness 3.17 mm
0.015 - 0.020 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 17.2 MPa
2500 psi
ASTM D 638
Elongation at Break >= 100 %
>= 100 %
ASTM D 638
Tensile Modulus 0.965 GPa
140 ksi
ASTM D 638
Flexural Strength 23.4 MPa
3400 psi
ASTM D 790
Flexural Modulus 0.827 GPa
120 ksi
ASTM D 790
Izod Impact, Notched 5.87 J/cm

@Thickness 3.17 mm
11.0 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched NB

@Thickness 3.17 mm
NB

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 43.3 °C
110 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 0.7937 mm
V-0

@Thickness 0.03125 in
5.50

@Thickness 0.200 mm
5.50

@Thickness 0.00787 in
Oxygen Index 27 %
27 %
ASTM D 2863
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 191 - 232 °C
375 - 450 °F
Mold Temperature 32.2 - 65.6 °C
90.0 - 150 °F
Drying Temperature 79.4 °C
175 °F
Dry Time 2 hour
2 hour
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi