RTP Company RTP 1483 HEC Polyethersulfone (PES), Nickel-Coated Carbon Fiber - EMI/RFI/ESD Protection

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 1483 HEC Polyethersulfone (PES), Nickel-Coated Carbon Fiber - EMI/RFI/ESD Protection.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.49 g/cc
1.49 g/cc
ASTM D 792
Filler Content 20 %
20 %
Primary Additive
Linear Mold Shrinkage 0.0015 cm/cm

@Thickness 3.17 mm
0.0015 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
ASTM D 638
Elongation at Break 1.3 %
1.3 %
ASTM D 638
Tensile Modulus 10.3 GPa
1500 ksi
ASTM D 638
Flexural Strength 193 MPa
28000 psi
ASTM D 790
Flexural Modulus 11.0 GPa
1600 ksi
ASTM D 790
Izod Impact, Notched 0.374 J/cm

@Thickness 3.17 mm
0.700 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 3.58 J/cm

@Thickness 3.17 mm
6.70 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity <= 10 ohm-cm
<= 10 ohm-cm
ASTM D 257
Surface Resistance <= 1000 ohm
<= 1000 ohm
ESD STM11.11
Surface Resistivity per Square <= 10000 ohm
<= 10000 ohm
ASTM D 257
Static Decay <= 2.0 sec
<= 2.0 sec
FTMS101C; 4046.1
Processing Properties Metric English Comments
Melt Temperature 343 - 377 °C
650 - 710 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C
300 °F
Dry Time 6 hour
6 hour
Moisture Content 0.040 %
0.040 %
Dew Point -31.7 °C
-25.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi