RTP Company RTP 1400.5 N Polyethersulfone (PES), Glass Fiber - High Viscosity

Category Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 10%Glass Fiber Filled
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 1400.5 N Polyethersulfone (PES), Glass Fiber - High Viscosity.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.39 g/cc
1.39 g/cc
ASTM D 792
Filler Content 5 %
5 %
Primary Additive
Linear Mold Shrinkage 0.0060 - 0.0080 cm/cm

@Thickness 3.17 mm
0.0060 - 0.0080 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 89.6 MPa
13000 psi
ASTM D 638
Elongation at Break 6.0 - 8.0 %
6.0 - 8.0 %
ASTM D 638
Tensile Modulus 3.45 GPa
500 ksi
ASTM D 638
Flexural Strength 131 MPa
19000 psi
ASTM D 790
Flexural Modulus 3.45 GPa
500 ksi
ASTM D 790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.17 mm
1.00 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 11.2 J/cm

@Thickness 3.17 mm
21.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Processing Properties Metric English Comments
Melt Temperature 343 - 377 °C
650 - 710 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C
300 °F
Dry Time 6 hour
6 hour
Moisture Content 0.040 %
0.040 %
Dew Point -31.7 °C
-25.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi