RTP Company RTP 1385 P-1 Polyphenylene Sulfide (PPS), Carbon Fiber

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 1385 P-1 Polyphenylene Sulfide (PPS), Carbon Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ASTM D 792
Filler Content 30 %
30 %
Primary Additive
Linear Mold Shrinkage 0.0010 cm/cm

@Thickness 3.17 mm
0.0010 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 207 MPa
30000 psi
ASTM D 638
Elongation at Break 1.1 %
1.1 %
ASTM D 638
Tensile Modulus 24.8 GPa
3600 ksi
ASTM D 638
Flexural Strength 283 MPa
41000 psi
ASTM D 790
Flexural Modulus 22.8 GPa
3300 ksi
ASTM D 790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.17 mm
1.00 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 4.11 J/cm

@Thickness 3.17 mm
7.70 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 268 °C
515 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity <= 1e+05
<= 1e+05
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 307 - 329 °C
585 - 625 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C
300 °F
Dry Time 6 hour
6 hour
Moisture Content 0.040 %
0.040 %
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi