RTP Company RTP 1385 C SI 2 Polyphenylene Sulfide (PPS), Carbon Fiber Reinforced - Silicone Lubricated

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 1385 C SI 2 Polyphenylene Sulfide (PPS), Carbon Fiber Reinforced - Silicone Lubricated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.44 g/cc
1.44 g/cc
ASTM D 792
Filler Content 30 %
30 %
Primary Additive
Linear Mold Shrinkage 0.00050 cm/cm

@Thickness 3.17 mm
0.00050 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 193 MPa
28000 psi
ASTM D 638
Elongation at Break 1.0 - 2.0 %
1.0 - 2.0 %
ASTM D 638
Tensile Modulus 26.2 GPa
3800 ksi
ASTM D 638
Flexural Strength 262 MPa
38000 psi
ASTM D 790
Flexural Modulus 22.8 GPa
3300 ksi
ASTM D 790
Izod Impact, Notched 0.747 J/cm

@Thickness 3.17 mm
1.40 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 4.27 J/cm

@Thickness 3.17 mm
8.00 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 260 °C
500 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity <= 1000 ohm-cm
<= 1000 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 302 - 343 °C
575 - 650 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 121 °C
250 °F
Dry Time 4 hour
4 hour
Injection Pressure 82.7 - 124 MPa
12000 - 18000 psi