RTP Company RTP 132 Polypropylene (PP), Talc

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Talc Filler
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 132 Polypropylene (PP), Talc.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D 792
Filler Content 30 %
30 %
Primary Additive
Linear Mold Shrinkage 0.0090 - 0.013 cm/cm

@Thickness 3.17 mm
0.0090 - 0.013 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 31.7 MPa
4600 psi
ASTM D 638
Elongation at Break >= 10 %
>= 10 %
ASTM D 638
Tensile Modulus 3.79 GPa
550 ksi
ASTM D 638
Flexural Strength 52.4 MPa
7600 psi
ASTM D 790
Flexural Modulus 3.17 GPa
460 ksi
ASTM D 790
Izod Impact, Notched 0.481 J/cm

@Thickness 3.17 mm
0.900 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 5.87 J/cm

@Thickness 3.17 mm
11.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 79.4 °C
175 °F
ASTM D 648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Processing Properties Metric English Comments
Melt Temperature 191 - 232 °C
375 - 450 °F
Mold Temperature 32.2 - 65.6 °C
90.0 - 150 °F
Drying Temperature 79.4 °C
175 °F
Dry Time 2 hour
2 hour
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi