RTP Company RTP 1307 D Polyphenylene Sulfide (PPS), Glass Fiber

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 40% Glass Fiber Filler
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 1307 D Polyphenylene Sulfide (PPS), Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.68 g/cc
1.68 g/cc
ASTM D 792
Additive Loading 40 %
40 %
Primary Additive
Linear Mold Shrinkage 0.0010 - 0.0020 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0020 in/in

@Thickness 0.125 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 179 MPa
26000 psi
ASTM D 638
Elongation at Break 1.9 %
1.9 %
ASTM D 638
Tensile Modulus 16.5 GPa
2400 ksi
ASTM D 638
Flexural Strength 255 MPa
37000 psi
ASTM D 790
Flexural Modulus 15.2 GPa
2200 ksi
ASTM D 790
Izod Impact, Notched 0.908 J/cm

@Thickness 3.17 mm
1.70 ft-lb/in

@Thickness 0.125 in
ASTM D 256
Izod Impact, Unnotched 5.61 J/cm

@Thickness 3.17 mm
10.5 ft-lb/in

@Thickness 0.125 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 266 °C
510 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 0.7937 mm
V-0

@Thickness 0.03125 in
Electrical Properties Metric English Comments
Volume Resistivity <= 1.00e+16 ohm-cm
<= 1.00e+16 ohm-cm
ASTM D 257
Dielectric Constant 3.8

@Frequency 1.00e+6 Hz
3.8

@Frequency 1.00e+6 Hz
Dry; ASTM D 150
Dielectric Strength 13.8 kV/mm
350 kV/in
short term, in oil; ASTM D 149
Dissipation Factor 0.0020

@Frequency 1.00e+6 Hz
0.0020

@Frequency 1.00e+6 Hz
Dry; ASTM D 150
Arc Resistance 120 sec
120 sec
ASTM D 495
Processing Properties Metric English Comments
Melt Temperature 307 - 329 °C
585 - 625 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C

@Time 21600 sec
300 °F

@Time 6.00 hour
Moisture Content 0.040 %
0.040 %
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi