RTP Company RTP 1300 D TFE 20 Polyphenylene Sulfide (PPS), PTFE Lubricated

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with PTFE Filler
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 1300 D TFE 20 Polyphenylene Sulfide (PPS), PTFE Lubricated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.47 g/cc
1.47 g/cc
ASTM D 792
Filler Content 20 %
20 %
Primary Additive
Linear Mold Shrinkage 0.010 - 0.018 cm/cm

@Thickness 3.17 mm
0.010 - 0.018 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 51.7 MPa
7500 psi
ASTM D 638
Elongation at Break 1.5 - 2.5 %
1.5 - 2.5 %
ASTM D 638
Tensile Modulus 3.45 GPa
500 ksi
ASTM D 638
Flexural Strength 100 MPa
14500 psi
ASTM D 790
Flexural Modulus 3.45 GPa
500 ksi
ASTM D 790
Izod Impact, Notched 0.267 J/cm

@Thickness 3.17 mm
0.500 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 2.67 J/cm

@Thickness 3.17 mm
5.00 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
265 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 302 - 343 °C
575 - 650 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 121 °C
250 °F
Dry Time 4 hour
4 hour
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi