- RTP Company PermaStat® 300 Polycarbonate (PC), ESD Protection - Permanently Anti-static - UL94 HB
RTP Company PermaStat® 300 Polycarbonate (PC), ESD Protection - Permanently Anti-static - UL94 HB
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | RTP Company |
| Trade Name | PermaStat® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RTP Company PermaStat® 300 Polycarbonate (PC), ESD Protection - Permanently Anti-static - UL94 HB.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D 792 |
| Linear Mold Shrinkage | 0.0060 - 0.0090 cm/cm @Thickness 3.17 mm |
0.0060 - 0.0090 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 44.8 MPa | 6500 psi | ASTM D 638 |
| Elongation at Break | >= 10 % | >= 10 % | ASTM D 638 |
| Tensile Modulus | 1.65 GPa | 240 ksi | ASTM D 638 |
| Flexural Strength | 62.1 MPa | 9000 psi | ASTM D 790 |
| Flexural Modulus | 1.79 GPa | 260 ksi | ASTM D 790 |
| Izod Impact, Notched | 6.41 J/cm @Thickness 3.17 mm |
12.0 ft-lb/in @Thickness 0.125 in |
D 256 |
| Izod Impact, Unnotched | NB @Thickness 3.17 mm |
NB @Thickness 0.125 in |
ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D 648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+8 - 1.00e+11 ohm-cm | 1.00e+8 - 1.00e+11 ohm-cm | ASTM D 257 |
| Surface Resistivity per Square | 1.00e+10 - 1.00e+12 ohm | 1.00e+10 - 1.00e+12 ohm | ASTM D 257 |
| Static Decay | <= 2.0 sec | <= 2.0 sec | MIL-PRF-81705D, 5kV to 50 V, 12% RH; FTMS101C; 4046.1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 221 - 243 °C | 430 - 470 °F | |
| Mold Temperature | 65.6 - 121 °C | 150 - 250 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | 0.020 % | 0.020 % | |
| Dew Point | -28.9 °C | -20.0 °F | |
| Injection Pressure | 41.4 - 68.9 MPa | 6000 - 10000 psi |
Users viewing this material also viewed the following:
- Pasargad Polymer Peyvand Pasalac 3P-H9000B ABS/PC
- LyondellBasell Alathon® M6030 High Density Polyethylene
- Karina 802-06/795-CRM Blue PVC Compound
- SABIC Innovative Plastics LNP STAT-KON RFD03 PA 66
- ExxonMobil 320 Mobil DTE PM Ashless
- ExxonMobil Mobil Rarus 827
- ChevronTexaco 68 Way Lubricant
- ExxonMobil Mobilgrease HTS
- RTP Company RTP 284 C TFE 15 Nylon 11 (PA); Carbon Fiber - PTFE Lubricated - 58% Renewable Resource Content
- RTP Company RTP 3400 G-430 Liquid Crystal Polymer (LCP), Glass Fiber - UL94 V-0
Copyright © lookpolymers.com All Rights Reserved