RTP Company ESD 683 Acrylonitrile Butadiene Styrene (ABS); Carbon Fiber - Electrically Conductive

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 20% Carbon Fiber Filled
Manufacturer RTP Company
Trade Name ESD
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company ESD 683 Acrylonitrile Butadiene Styrene (ABS); Carbon Fiber - Electrically Conductive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D 792
Additive Loading 20 %
20 %
Primary Additive
Linear Mold Shrinkage 0.00050 - 0.0020 cm/cm

@Thickness 3.20 mm
0.00050 - 0.0020 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 107 MPa
15500 psi
ASTM D 638
Elongation at Break 1.0 - 1.5 %
1.0 - 1.5 %
ASTM D 638
Tensile Modulus 13.8 GPa
2000 ksi
ASTM D 638
Flexural Strength 152 MPa
22000 psi
ASTM D 790
Flexural Modulus 11.7 GPa
1700 ksi
ASTM D 790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.20 mm
1.00 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 2.67 J/cm

@Thickness 3.20 mm
5.00 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Electrical Properties Metric English Comments
Volume Resistivity <= 100 ohm-cm
<= 100 ohm-cm
ASTM D 257
Surface Resistance <= 1000 ohm
<= 1000 ohm
ESD STM11.11
Surface Resistivity per Square <= 10000 ohm
<= 10000 ohm
ASTM D 257
Static Decay <= 0.50 sec
<= 0.50 sec
FTMS101C; 4046.1
Processing Properties Metric English Comments
Melt Temperature 204 - 238 °C
400 - 460 °F
Mold Temperature 62.8 - 85.0 °C
145 - 185 °F
Drying Temperature 82.2 °C

@Time 7200 sec
180 °F

@Time 2.00 hour
Moisture Content 0.10 %
0.10 %
Dew Point -17.8 °C
0.000 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi