RTP Company ESD 1385 Polyphenylene Sulfide (PPS); Carbon Fiber - Electrically Conductive

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 30% Carbon Fiber Filler
Manufacturer RTP Company
Trade Name ESD
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company ESD 1385 Polyphenylene Sulfide (PPS); Carbon Fiber - Electrically Conductive.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ASTM D 792
Additive Loading 30 %
30 %
Primary Additive
Linear Mold Shrinkage 0.00050 - 0.0015 cm/cm

@Thickness 3.20 mm
0.00050 - 0.0015 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 172 MPa
25000 psi
ASTM D 638
Elongation at Break 0.50 - 1.5 %
0.50 - 1.5 %
ASTM D 638
Tensile Modulus 24.8 GPa
3600 ksi
ASTM D 638
Flexural Strength 234 MPa
34000 psi
ASTM D 790
Flexural Modulus 22.1 GPa
3200 ksi
ASTM D 790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.20 mm
1.00 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 3.47 J/cm

@Thickness 3.20 mm
6.50 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 268 °C
515 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity <= 100 ohm-cm
<= 100 ohm-cm
ASTM D 257
Surface Resistance <= 1000 ohm
<= 1000 ohm
ESD STM11.11
Surface Resistivity per Square <= 10000 ohm
<= 10000 ohm
ASTM D 257
Static Decay <= 0.50 sec
<= 0.50 sec
FTMS101C; 4046.1
Processing Properties Metric English Comments
Melt Temperature 307 - 329 °C
585 - 625 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C

@Time 21600 sec
300 °F

@Time 6.00 hour
Moisture Content 0.040 %
0.040 %
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi