RTP Company EMI 861 TFE 8 Acetal (POM) Stainless Steel Fiber - PTFE Lubricated - Electrically Conductive - EMI/RFI Shielding

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Steel Filled
Manufacturer RTP Company
Trade Name EMI
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company EMI 861 TFE 8 Acetal (POM) Stainless Steel Fiber - PTFE Lubricated - Electrically Conductive - EMI/RFI Shielding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Preliminary Data Sheet
Physical Properties Metric English Comments
Specific Gravity 1.53 g/cc
1.53 g/cc
ASTM D 792
Additive Loading 10 %
10 %
Primary Additive
Linear Mold Shrinkage 0.010 - 0.030 cm/cm

@Thickness 3.20 mm
0.010 - 0.030 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.2 MPa
8000 psi
ASTM D 638
Elongation at Break >= 10 %
>= 10 %
ASTM D 638
Tensile Modulus 2.41 GPa
350 ksi
ASTM D 638
Flexural Strength 75.8 MPa
11000 psi
ASTM D 790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D 790
Izod Impact, Notched 0.801 J/cm

@Thickness 3.20 mm
1.50 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 7.47 J/cm

@Thickness 3.20 mm
14.0 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 94.4 °C
202 °F
ASTM D 648
Electrical Properties Metric English Comments
Volume Resistivity <= 10 ohm-cm
<= 10 ohm-cm
ASTM D 257
Surface Resistance <= 10000 ohm
<= 10000 ohm
ESD STM11.11
Surface Resistivity per Square <= 1e+05
<= 1e+05
ASTM D 257
Static Decay <= 0.50 sec
<= 0.50 sec
FTMS101C; 4046.1
Processing Properties Metric English Comments
Melt Temperature 199 - 218 °C
390 - 425 °F
Mold Temperature 82.2 - 107 °C
180 - 225 °F
Drying Temperature 121 °C

@Time 7200 sec
250 °F

@Time 2.00 hour
Moisture Content 0.15 %
0.15 %
Dew Point -28.9 °C
-20.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi