Quantum Nylon 6/6 30% Glass Fiber Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Quantum Advanced Engineering Plastics
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Quantum Nylon 6/6 30% Glass Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Quantum Advanced Engineering Plastics
Physical Properties Metric English Comments
Specific Gravity 1.34 g/cc
1.34 g/cc
ASTM D792
Water Absorption 0.70 %
0.70 %
ASTM D570
Water Absorption at Saturation 5.5 %
5.5 %
ASTM D570
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100
100
ASTM D785
Hardness, Rockwell R 122
122
ASTM D785
Hardness, Shore D 80
80
ASTM 2240
Tensile Strength 159 MPa
23000 psi
ASTM D638
Elongation at Break 6.0 %
6.0 %
ASTM D638
Tensile Modulus 8.27 GPa
1200 ksi
ASTM D638
Flexural Strength 110 MPa
16000 psi
ASTM D790
Flexural Modulus 0.758 GPa
110 ksi
ASTM D790
Compressive Strength 138 MPa
20000 psi
ASTM D695
Izod Impact, Notched 1.07 J/cm
2.00 ft-lb/in
ASTM D256
Coefficient of Friction 0.31
0.31
Thermal Properties Metric English Comments
CTE, linear 27.0 µm/m-°C
15.0 µin/in-°F
ASTM D696
Thermal Conductivity 0.288 W/m-K
2.00 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 260 °C
500 °F
ASTM D3417
Maximum Service Temperature, Air 104 °C
220 °F
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 252 °C
485 °F
ASTM D648
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Dielectric Constant 3.6

@Frequency 1.00e+6 Hz
3.6

@Frequency 1.00e+6 Hz
ASTM D150
Dielectric Strength 13.8 kV/mm
350 kV/in
ASTM D149
Dissipation Factor 0.0016

@Frequency 1.00e+6 Hz
0.0016

@Frequency 1.00e+6 Hz
ASTM D150
Descriptive Properties Value Comments
FDA Compliance no
Copyright © lookpolymers.com All Rights Reserved