Quantum Composites QC-8816 66% Glass Fiber Reinforced Polyester Hybrid SMC

Category Polymer , Thermoset , Composite SMC , Polyester, TS , Thermoset Polyester Glass SMC
Manufacturer Quantum Composites
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Quantum Composites QC-8816 66% Glass Fiber Reinforced Polyester Hybrid SMC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
QC-8816 is a polyester hybrid engineered structural composite molding compound reinforced with continuous, unidirectional (0°) glass fibers. It provides high strength, stiffness and fatigue resistance in the fiber direction, and can be used to selectively reinforce other materials.Form = Rolled SheetColor = Black, NaturalGlass Fiber Content = 66% nominalGlass Fiber Length = ContinuousInformation provided by Quantum Composites.
Physical Properties Metric English Comments
Specific Gravity 1.95 g/cc
1.95 g/cc
ASTM D792
Linear Mold Shrinkage 0.00 cm/cm
0.00 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Barcol 68
68
ASTM D2583
Tensile Strength 483 MPa
70100 psi
ASTM D638
Flexural Strength 931 MPa
135000 psi
ASTM D790
Flexural Modulus 34.5 GPa
5000 ksi
ASTM D790
Izod Impact, Notched 22.24 J/cm
41.66 ft-lb/in
ASTM D256
Processing Properties Metric English Comments
Processing Temperature 132 - 149 °C

@Thickness 12.7 mm
270 - 300 °F

@Thickness 0.500 in
Compression Molding
Clamp Pressure 2.07 - 6.89 MPa
300 - 1000 psi
Cure Time 3.00 - 5.00 min

@Thickness 6.35 mm,
Temperature 138 °C
0.0500 - 0.0833 hour

@Thickness 0.250 in,
Temperature 280 °F
Shelf Life 2.00 Month

@Temperature 23.9 °C
2.00 Month

@Temperature 75.0 °F