Quantum Composites HTC-9590 55% Carbon Fiber Reinforced Bismaleimide SMC, High Temperature Composite

Category Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Composite SMC , Polyimide, TS
Manufacturer Quantum Composites
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Quantum Composites HTC-9590 55% Carbon Fiber Reinforced Bismaleimide SMC, High Temperature Composite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
HTC-9590 (127-51-3) is a 12K Pan Based Carbon Fiber reinforced Bismaleimide (BMI) ESC (Engineered Structural Composite) molding compound. It exhibits outstanding elevated temperature characteristics providing greatly extended service temperature range versus epoxy compounds for compression molding applications.Form = Roll SheetColor = Natural (Black)Carbon Fiber Content = 55% nominalInformation provided by Quantum Composites.
Physical Properties Metric English Comments
Specific Gravity 1.55 g/cc
1.55 g/cc
ASTM D792
Linear Mold Shrinkage 0.0015 cm/cm
0.0015 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength 131 MPa
19000 psi
ASTM D638
Tensile Modulus 48.3 GPa
7010 ksi
ASTM D638
Flexural Strength 496 MPa
71900 psi
ASTM D790
Flexural Modulus 48.3 GPa
7010 ksi
ASTM D790
Izod Impact, Notched 14.41 J/cm
27.00 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Glass Transition Temp, Tg 341 °C
646 °F
wet; ASTM D4065
379 °C
714 °F
dry; ASTM D4065
Processing Properties Metric English Comments
Shelf Life 1.00 Month

@Temperature 4.44 °C
1.00 Month

@Temperature 40.0 °F
6.00 Month

@Temperature -12.2 °C
6.00 Month

@Temperature 10.0 °F
Descriptive Properties Value Comments
Fiber Length (in) 1
Carbon, nominal