Quantum Composites HTC-9500 55% E-Glass Fiber Reinforced Bismaleimide SMC, High Temperature Composite

Category Polymer , Thermoset , Composite SMC , Polyimide, TS
Manufacturer Quantum Composites
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Quantum Composites HTC-9500 55% E-Glass Fiber Reinforced Bismaleimide SMC, High Temperature Composite.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
HTC-9500 (127-51-6) is an E-Glass Fiber reinforced Bismaleimide (BMI) ESC (Engineered Structural Composite) molding compound. It exhibits outstanding elevated temperature characteristics providing greatly extended service temperature range versus epoxy compounds for compression molding applications.Form = Rolled SheetColor = NaturalGlass Fiber Content = 55% nominalInformation provided by Quantum Composites.
Physical Properties Metric English Comments
Specific Gravity 1.82 g/cc
1.82 g/cc
ASTM D792
Linear Mold Shrinkage 0.0015 cm/cm
0.0015 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength 196 MPa
28400 psi
ASTM D638
Tensile Modulus 33.8 GPa
4900 ksi
ASTM D638
Flexural Strength 648 MPa
94000 psi
ASTM D790
Flexural Modulus 27.6 GPa
4000 ksi
ASTM D790
Processing Properties Metric English Comments
Shelf Life 1.00 Month

@Temperature 4.44 °C
1.00 Month

@Temperature 40.0 °F
6.00 Month

@Temperature -12.2 °C
6.00 Month

@Temperature 10.0 °F
Descriptive Properties Value Comments
Fiber Length (in) 1
E-Glass, nominal