Quantum Acetal-Homopolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Homopolymer, Unreinforced |
| Manufacturer | Quantum Advanced Engineering Plastics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Quantum Acetal-Homopolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Quantum Advanced Engineering Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Water Absorption | 0.25 % | 0.25 % | ASTM D570 |
| Water Absorption at Saturation | 0.90 % | 0.90 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 94 | 94 | ASTM D785 |
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Hardness, Shore D | 85 | 85 | ASTM 2240 |
| Tensile Strength | 68.9 MPa | 10000 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ASTM D638 |
| Flexural Strength | 96.5 MPa | 14000 psi | ASTM D790 |
| Flexural Modulus | 2.90 GPa | 420 ksi | ASTM D790 |
| Compressive Strength | 110 MPa | 16000 psi | ASTM D695 |
| Compressive Modulus | 3.10 GPa | 450 ksi | ASTM D695 |
| Shear Strength | 62.1 MPa | 9000 psi | ASTM D732 |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Coefficient of Friction | 0.20 | 0.20 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 99.0 µm/m-°C | 55.0 µin/in-°F | ASTM D696 |
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 175 °C | 347 °F | ASTM D3417 |
| Maximum Service Temperature, Air | 85.0 °C | 185 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 166 °C | 330 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 |
| Dissipation Factor | 0.0048 @Frequency 1.00e+6 Hz |
0.0048 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FDA Compliance | yes |
Users viewing this material also viewed the following:
- Solvay Specialty Polymers Veradel® 3200 Polyethersulfone (PESU) (Unverified Data**)
- Techmer ES HiFill® PP 0112 B AM2 Polypropylene
- Techmer ES HiFill® TPX-HTN-02028 A 60% Glass Filled
- A. Schulman POLYTROPE™ TPP 524 Injection Molding Grade Olefinic Thermoplastic Elastomer
- Zeon Chemicals Zeonex® 330R Cyclo-Olefin Polymer
- Arlon Ultrapad™ 55072R125D 0.125" (3.17 mm) Cured Silicone Rubber with Fiberglass Substrate
- Azdel AZMET® CM20350 35% continuous random fiber mat / PBT resin matrix
- 3M Scotch-Weld™ SI40 Surface Insensitive Instant Adhesive
- PolyOne Synprene® ST-6110 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved