Protective Coating PC-Rot Terminator® Epoxy Wood Consolidant

Category Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive
Manufacturer Protective Coating Co.
Trade Name PC-Rot Terminator®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Protective Coating PC-Rot Terminator® Epoxy Wood Consolidant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: PC-Rot Terminator® is designed to strengthen decayed or rotted wood. The mixture is a low viscosity liquid that penetrates porous surfaces filling and sealing voids with an epoxy that cures to a hard but durable component. Rot Terminator® combines an extended open time and low viscosity without solvents. The Rot Terminator® is useful for replacement of missing wood fibers or wood resin. It fills the void in the wood with an elastomer that has strength greater than wood. Typical wood resin has low tensile and compressive properties when compared to cured epoxy polymer in wood. The epoxy act as a binder that glues the wood fibers together. The wood fibers become much stronger in combination with the epoxy elastomer. It is mixed one part hardener to two parts resin.
Physical Properties Metric English Comments
Viscosity 300 cP

@Temperature 25.0 °C
300 cP

@Temperature 77.0 °F
Hardener
500 cP

@Temperature 25.0 °C
500 cP

@Temperature 77.0 °F
Mixed
600 cP

@Temperature 25.0 °C
600 cP

@Temperature 77.0 °F
Resin
Mechanical Properties Metric English Comments
Hardness, Shore D 78
78
Tensile Strength, Ultimate 31.0 MPa
4500 psi
Elongation at Break 12 %
12 %
Tensile Modulus 1.45 GPa
210 ksi
Flexural Strength 65.5 MPa
9500 psi
Flexural Modulus 2.07 GPa
300 ksi
Compressive Yield Strength 44.8 MPa
6500 psi
Compressive Modulus 1.59 GPa
230 ksi
Thermal Properties Metric English Comments
Flash Point 103 °C
217 °F
Hardener, closed cup
177 °C
351 °F
Resin, closed cup
Optical Properties Metric English Comments
Gardner Color Number 3.0
3.0
Resin
5.0
5.0
Mix
8.0
8.0
Hardener
Processing Properties Metric English Comments
Cure Time 1440 min
24.0 hour
60.0 min

@Temperature 25.0 °C
1.00 hour

@Temperature 77.0 °F
720 min

@Temperature 25.0 °C
12.0 hour

@Temperature 77.0 °F
Thin Film Set
10100 min

@Temperature 25.0 °C
168 hour

@Temperature 77.0 °F
Maximum Cure
Descriptive Properties Value Comments
Mar Resistance 1.05 kg