Premix Thermoplastics PRE-ELEC® TPE 1502 Conductive Thermoplastic Compound

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	Premix Thermoplastics Inc.
Trade Name	PRE-ELEC®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Premix Thermoplastics PRE-ELEC® TPE 1502 Conductive Thermoplastic Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PRE-ELEC® TPE 1502 is a conductive thermoplastic compound based on a thermoplastic elastomer (TPE). Conductivity is achieved by using a special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® TPE 1502 has retained the excellent mechanical properties of the base elastomer.Applications: Extruded profiles, sheets and injection moulded technical parts.Processing: PRE-ELEC® TPE 1502 compound can be extruded or injection moulded in the machines using normal processing conditions as with TPE.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY

Physical Properties	Metric	English	Comments
Density	1.08 g/cc	0.0390 lb/in³
Thickness	102 microns	4.00 mil
Linear Mold Shrinkage	0.021 cm/cm	0.021 in/in	ISO 294-4
Melt Flow	4.0 g/10 min @Load 10.0 kg, Temperature 190 °C	4.0 g/10 min @Load 22.0 lb, Temperature 374 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	65	65	ISO 868
Tensile Strength	4.20 MPa	609 psi	ISO 527
	1.90 MPa @Strain 100 %	276 psi @Strain 100 %	ISO 527
	2.50 MPa @Strain 200 %	363 psi @Strain 200 %	ISO 527
	3.10 MPa @Strain 300 %	450 psi @Strain 300 %	ISO 527
Tensile Strength, Yield	1.90 MPa	276 psi	ISO 527
Elongation at Break	650 %	650 %	ISO 527

Electrical Properties	Metric	English	Comments
Volume Resistivity	<= 100 ohm-cm	<= 100 ohm-cm	ISO D-257

Processing Properties	Metric	English	Comments
Zone 1	170 °C	338 °F	Cylinder
	210 °C	410 °F	Die
Zone 2	180 °C	356 °F	Cylinder
	210 °C	410 °F	Die
Zone 3	190 °C	374 °F	Cylinder
	210 °C	410 °F	Die
Zone 4	200 °C	392 °F	Cylinder
	210 °C	410 °F	Die
Zone 5	210 °C	410 °F	Die
	210 °C	410 °F	Cylinder
Melt Temperature	180 - 210 °C	356 - 410 °F
Mold Temperature	30.0 - 50.0 °C	86.0 - 122 °F
Roll Temperature	50.0 °C	122 °F	3rd Roll
	60.0 °C	140 °F	1st Roll
	60.0 °C	140 °F	2nd Roll
Drying Temperature	<= 65.0 °C	<= 149 °F	Pre-drying
Dry Time	1 - 2 hour	1 - 2 hour
Shelf Life	12.0 Month	12.0 Month	Normal Storing Conditions

Descriptive Properties	Value	Comments
Injection Pressure (psi)	Low-Medium
Injection Speed	Medium-High