Premix Thermoplastics PRE-ELEC® PPE 1462  (discontinued **)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® PPE 1462  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC PPE 1462 is a conductive thermoplastic compound based on modified polyphenylene ether (PPE). Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PPE 1462 has an excellent balance of mechanical properties and is easy to injection mould.Typical applications include injection molded IC-trays and technical parts where a high heat resistance is needed. Test Specimen - 4.0 mm thick, 10.0 mm wide molded rod.Information provided by Premix Thermoplastics Inc.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
Linear Mold Shrinkage 0.0060 - 0.0090 cm/cm
0.0060 - 0.0090 in/in
ISO 294-4
Melt Flow 2.0 g/10 min

@Load 5.00 kg,
Temperature 300 °C
2.0 g/10 min

@Load 11.0 lb,
Temperature 572 °F
ISO 1133
High Load Melt Index 21 g/10 min

@Load 21.6 kg,
Temperature 300 °C
21 g/10 min

@Load 47.6 lb,
Temperature 572 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 89
89
ISO 868
Tensile Strength, Ultimate 65.0 MPa
9430 psi
ISO 527
Elongation at Break 7.0 %
7.0 %
ISO 527
Modulus of Elasticity 3.00 GPa
435 ksi
ISO 178
Izod Impact, Notched 0.200 J/cm

@Thickness 4.00 mm,
Temperature -20.0 °C
0.375 ft-lb/in

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
0.370 J/cm

@Thickness 4.00 mm,
Temperature 23.0 °C
0.693 ft-lb/in

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched 2.00 J/cm

@Thickness 4.00 mm,
Temperature -20.0 °C
3.75 ft-lb/in

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
4.20 J/cm

@Thickness 4.00 mm,
Temperature 23.0 °C
7.87 ft-lb/in

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 170 °C
338 °F
ISO 75/Method Bf
Vicat Softening Point 180 °C
356 °F
Rate B; ISO 306/B50
187 °C
369 °F
Rate A; ISO 306/A50
Glass Transition Temp, Tg 177 °C
351 °F
T<sub>g</sub>(Amorphous)
Electrical Properties Metric English Comments
Volume Resistivity <= 1e+05
<= 1e+05
ISO D-257
Surface Resistance <= 1.00e+6 ohm
<= 1.00e+6 ohm
ISO D-257
Processing Properties Metric English Comments
Melt Temperature 290 - 320 °C
554 - 608 °F
Mold Temperature 90.0 - 130 °C
194 - 266 °F
Drying Temperature 60.0 - 80.0 °C

@Time 7200 - 14400 sec
140 - 176 °F

@Time 2.00 - 4.00 hour
Pre-drying
Moisture Content <= 0.15 %
<= 0.15 %
When Produced
Injection Pressure 180.0 - 230.0 MPa
26110 - 33360 psi
Hold Pressure 150.0 - 170.0 MPa
21760 - 24660 psi
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions
Descriptive Properties Value Comments
Appearance Granule
Color Black
Injection Speed Moderate - Fast