Premix Thermoplastics PRE-ELEC® PET 1451
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Premix Thermoplastics Inc. |
| Trade Name | PRE-ELEC® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Premix Thermoplastics PRE-ELEC® PET 1451.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PRE-ELEC PET 1451 is a conductive thermoplastic compound based on PETG. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PET 1451 has excellent mechanical properties and is easy to extrude.Typical applications include extruded and co-extruded sheets for thermoforming of trays and micro chip carrier tape.Information provided by Premix Thermoplastics Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | 4 mm thick, 10.0 mm wide molded rod; ISO 294-4 |
| Melt Flow | 4.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
4.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| High Load Melt Index | 28 g/10 min @Load 21.6 kg, Temperature 200 °C |
28 g/10 min @Load 47.6 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 32.0 MPa | 4640 psi | ISO 527 |
| Film Elongation at Break, MD | 44 % | 44 % | ISO 527 |
| Film Elongation at Yield, MD | 4.0 % | 4.0 % | ISO 527 |
| Modulus of Elasticity | 2.60 GPa | 377 ksi | 4 mm thick;10.0 mm wide molded rod; ISO 178 |
| Izod Impact, Notched | 1.20 J/cm @Thickness 4.00 mm, Temperature 23.0 °C |
2.25 ft-lb/in @Thickness 0.157 in, Temperature 73.4 °F |
ISO 180 |
| Izod Impact, Unnotched | NB @Thickness 4.00 mm, Temperature 23.0 °C |
NB @Thickness 0.157 in, Temperature 73.4 °F |
ISO 180 |
| Film Tensile Strength at Break, MD | 31.0 MPa | 4500 psi | ISO 527 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | 4 mm thick;10.0 mm wide molded rod; ISO 75/Method Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | 4 mm thick;10.0 mm wide molded rod; ISO 75/Method Af |
| Vicat Softening Point | 70.0 °C | 158 °F | Rate A; 4 mm thick;10.0 mm wide molded rod; ISO 306/A50 |
| 75.0 °C | 167 °F | Rate B; 4 mm thick;10.0 mm wide molded rod; ISO 306/B50 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | <= 1000 ohm-cm | <= 1000 ohm-cm | 400 um thick sheet; ISO D-257 |
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | 400 um thick sheet; ISO D-257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 210 °C | 410 °F | Zone 1; Cylinder |
| 220 °C | 428 °F | Zone 4; Cylinder | |
| 220 °C | 428 °F | Zone 5; Cylinder | |
| 220 °C | 428 °F | Zone 2; Cylinder | |
| 220 °C | 428 °F | Zone 3; Cylinder | |
| 230 °C | 446 °F | Zone 6; Cylinder | |
| Die Temperature | 215 °C | 419 °F | Zone 3 |
| 225 °C | 437 °F | Zone 2 | |
| 225 °C | 437 °F | Zone 4 | |
| 230 °C | 446 °F | Zone 5 | |
| 230 °C | 446 °F | Zone 1 | |
| Roll Temperature | 60.0 °C | 140 °F | 3rd Roll |
| 80.0 °C | 176 °F | 2nd Roll | |
| 90.0 °C | 194 °F | 1st Roll | |
| Drying Temperature | 65.0 °C @Time 14400 sec |
149 °F @Time 4.00 hour |
Pre-drying |
| Moisture Content | <= 0.15 % | <= 0.15 % | When Produced |
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Granule | |
| Color | Black |