Premix Thermoplastics PRE-ELEC® ESD 6300 Static Dissipative Thermoplastic Compound

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer Premix Thermoplastics Inc.
Trade Name PRE-ELEC®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® ESD 6300 Static Dissipative Thermoplastic Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC® ESD 6300 is a static dissipative thermoplastic compound based on high impact polystyrene. The dissipative property is permanent and built into the polymer chain. PRE-ELEC® ESD6300 has been developed for extrusion of thermoformable multilayer sheets and injection molding. Surface resistance values of 108 O (EOS/ESD S11.11-1993, IEC 61340-5-1) can be achieved with optimum processing parameters. The products made out of PRE-ELEC® ESD 6300 are washable, reusable, recyclable. PRE-ELEC® ESD 6300 is whitish in colour and can be coloured into various bright colours.Applications: Injection moulded boxes, bins, thermoformed trays and clamshells when permanent ESD protection is required. These products can be used in electronics, medical, pharmaceutical and paper handling industries. The performace of ESD 6300 in coextrustion can further be improved by adding ~5% of SBS. This improves the ductility of the outer layer and the adnesion between the layersProcessing: PRE-ELEC® ESD 6300 compound can be processed in normal processing conditions as with polystyrene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
Physical Properties Metric English Comments
Density 1.07 g/cc
0.0387 lb/in³
Thickness 102 microns
4.00 mil
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ISO 294-4
Melt Flow 11 g/10 min

@Load 5.00 kg,
Temperature 200 °C
11 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength 14.0 MPa
2030 psi
ISO 527
Tensile Strength, Yield 16.0 MPa
2320 psi
ISO 527
Elongation at Break 12 %
12 %
ISO 527
Elongation at Yield 4.0 %
4.0 %
ISO 527
Modulus of Elasticity 1.20 GPa
174 ksi
ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
1.90 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched (ISO) 24.0 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
11.4 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 81.0 °C
178 °F
75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi) 69.0 °C
156 °F
75/Method Af
Electrical Properties Metric English Comments
Surface Resistance <= 1.00e+9 ohm

@Thickness 0.00100 mm
<= 1.00e+9 ohm

@Thickness 0.0000394 in
ISO IEC 61340-5-1
Static Decay <= 1.0 sec

@Thickness 1.00 mm
<= 1.0 sec

@Thickness 0.0394 in
ISO IEC 61340-5-1
Processing Properties Metric English Comments
Zone 1 180 °C
356 °F
Cylinder
200 °C
392 °F
Die
Zone 2 190 °C
374 °F
Cylinder
200 °C
392 °F
Die
Zone 3 190 °C
374 °F
Die
200 °C
392 °F
Cylinder
Zone 4 200 °C
392 °F
Die
200 °C
392 °F
Cylinder
Zone 5 200 °C
392 °F
Die
200 °C
392 °F
Cylinder
Melt Temperature 190 - 210 °C
374 - 410 °F
Mold Temperature 30.0 - 70.0 °C
86.0 - 158 °F
Roll Temperature 50.0 °C
122 °F
3rd Roll
60.0 °C
140 °F
1st Roll
60.0 °C
140 °F
2nd Roll
Drying Temperature 70.0 - 80.0 °C
158 - 176 °F
Pre-drying in a dehumidifier
Dry Time 3 - 4 hour
3 - 4 hour
Injection Pressure 75.2 - 120 MPa
10900 - 17400 psi
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions
Descriptive Properties Value Comments
Injection Speed Moderate