Premix Thermoplastics PRE-ELEC® ESD 5510 Static Dissipative Thermoplastic Compound

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer Premix Thermoplastics Inc.
Trade Name PRE-ELEC®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® ESD 5510 Static Dissipative Thermoplastic Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC® ESD 5510 is a static dissipative thermoplastic compound based on polypropylene. The dissipative property is permanent and built into the polymer chain. PRE-ELEC® ESD 5510 can be injection moulded, extruded, blow moulded and blown into film. Surface resistance values of 109 O (EOS/ESD S11.11-1993, IEC 61340-5-1) can be achieved. The products made out of PRE-ELEC® ESD 5510 are washable, reusable and recyclable. PRE-ELEC® ESD 5510 is designed for clean applications with extremely low amount of extractable ions. The melt flow properties of PRE-ELEC® ESD 5510 are tailored to fit the requirements of (co)extrusion.Applications: Bins, trays, bottles and bags where permanent ESD protection and high cleanliness are required. These products can be used mainly in electronics packaging, but in many other application areas as well. Processing: PRE-ELEC® ESD 5510 compound can be processed in normal processing conditions as with polypropylene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
Physical Properties Metric English Comments
Density 0.920 g/cc
0.0332 lb/in³
Thickness 102 microns
4.00 mil
Linear Mold Shrinkage 0.016 cm/cm
0.016 in/in
ISO 294-4
Melt Flow 3.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
3.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength 10.0 MPa
1450 psi
ISO 527
Tensile Strength, Yield 20.0 MPa
2900 psi
ISO 527
Elongation at Break 700 %
700 %
ISO 527
Elongation at Yield 15 %
15 %
ISO 527
Tensile Modulus 0.250 GPa
36.3 ksi
ISO 527
Flexural Modulus 1.00 GPa
145 ksi
ISO 178
Izod Impact, Notched (ISO) 56.0 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
26.6 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched (ISO) NB

@Thickness 4.00 mm,
Temperature 23.0 °C
NB

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 80.0 °C
176 °F
75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
75/Method Af
Vicat Softening Point 135 °C
275 °F
ISO 306/A50
Flammability, UL94 HB

@Thickness 1.00 mm
HB

@Thickness 0.0394 in
RD524
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
RD524
Electrical Properties Metric English Comments
Surface Resistance 1.00e+9 ohm
1.00e+9 ohm
ISO IEC 61340-5-1
Static Decay <= 1.0 sec
<= 1.0 sec
ISO IEC 61340-5-1
Processing Properties Metric English Comments
Zone 1 180 °C
356 °F
Cylinder
210 °C
410 °F
Die
Zone 2 190 °C
374 °F
Cylinder
210 °C
410 °F
Die
Zone 3 200 °C
392 °F
Die
200 °C
392 °F
Cylinder
Zone 4 210 °C
410 °F
Die
210 °C
410 °F
Cylinder
Zone 5 210 °C
410 °F
Die
210 °C
410 °F
Cylinder
Melt Temperature 190 - 210 °C
374 - 410 °F
Mold Temperature 30.0 - 40.0 °C
86.0 - 104 °F
Roll Temperature 40.0 °C
104 °F
2nd Roll
40.0 °C
104 °F
3rd Roll
50.0 °C
122 °F
1st Roll
Drying Temperature 60.0 - 80.0 °C
140 - 176 °F
Pre-drying in a dehumidifier
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 60.0 - 80.0 MPa
8700 - 11600 psi
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions
Descriptive Properties Value Comments
Injection Speed Moderate