Premix Thermoplastics PRE-ELEC® ESD 1100  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® ESD 1100  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC ESD 1100 is a static dissipative thermoplastic compound based on PETG. The dissipative property is permanent and built into the polymer chain. PRE-ELEC ESD 1100 has been developed for the extrusion of mono- or multi-layer sheet for thermoforming. The thermoformed products of PRE-ELEC ESD 1100 are washable, reusable and recyclable. Surface resistance values of 108 ohms (EOS/ESD S11.11-1993, IEC 61340-5-1) can be achieved with optimum processing parameters.Typical applications are extruded sheet for vacuum forming of trays which give permanent ESD protection for the electronics (hard disk), medical and pharmaceutical industries. PRE-ELEC ESD 1100 can also be injection molded and colored into various bright colors.Information provided by Premix Thermoplastics Inc.
Physical Properties Metric English Comments
Density 1.25 g/cc
0.0452 lb/in³
Thickness 406 microns
16.0 mil
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm

@Thickness 4.00 mm
0.0040 - 0.0060 in/in

@Thickness 0.157 in
10.0 mm wide molded rod; ISO 294-4
Melt Flow 5.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
5.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ISO 1133
High Load Melt Index 35 g/10 min

@Load 21.6 kg,
Temperature 200 °C
35 g/10 min

@Load 47.6 lb,
Temperature 392 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore A 99

@Thickness 4.00 mm
99

@Thickness 0.157 in
10.0 mm wide molded rod; ISO 868
Film Tensile Strength at Yield, MD 40.0 MPa
5800 psi
ISO 527
Film Tensile Strength at Yield, TD 30.0 MPa
4350 psi
ISO 527
Film Elongation at Break, MD 350 %
350 %
ISO 527
Film Elongation at Break, TD 300 %
300 %
ISO 527
Film Elongation at Yield, MD 5.0 %
5.0 %
ISO 527
Film Elongation at Yield, TD 4.0 %
4.0 %
ISO 527
Modulus of Elasticity 1.65 GPa

@Thickness 4.00 mm
239 ksi

@Thickness 0.157 in
10.0 mm wide molded rod; ISO 178
Izod Impact, Notched 0.230 J/cm

@Thickness 4.00 mm,
Temperature 23.0 °C
0.431 ft-lb/in

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched NB

@Thickness 4.00 mm,
Temperature 23.0 °C
NB

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Film Tensile Strength at Break, MD 50.0 MPa
7250 psi
ISO 527
Film Tensile Strength at Break, TD 35.0 MPa
5080 psi
ISO 527
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 67.0 °C

@Thickness 4.00 mm
153 °F

@Thickness 0.157 in
10.0 mm wide molded rod; ISO 75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C

@Thickness 4.00 mm
140 °F

@Thickness 0.157 in
10.0 mm wide molded rod; ISO 75/Method Af
Vicat Softening Point 72.0 °C

@Thickness 4.00 mm
162 °F

@Thickness 0.157 in
Rate A; 10.0 mm wide molded rod; ISO 306/B50
82.0 °C

@Thickness 4.00 mm
180 °F

@Thickness 0.157 in
Rate A; 10.0 mm wide molded rod; ISO 306/A50
Flammability, UL94 HB

@Thickness 1.00 mm
HB

@Thickness 0.0394 in
ISO RD524
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
ISO RD524
Electrical Properties Metric English Comments
Surface Resistance <= 1.00e+10 ohm
<= 1.00e+10 ohm
400 um thick sheet; ISO IEC 61340-5-1
Static Decay <= 1.0 sec
<= 1.0 sec
400 um thick sheet; ISO IEC 61340-5-1
Processing Properties Metric English Comments
Middle Barrel Temperature 190 °C
374 °F
Zone 2; Cylinder
190 °C
374 °F
Zone 1; Cylinder
200 °C
392 °F
Zone 6; Cylinder
200 °C
392 °F
Zone 4; Cylinder
200 °C
392 °F
Zone 5; Cylinder
200 °C
392 °F
Zone 3; Cylinder
Die Temperature 179 °C
355 °F
Zone 3
188 °C
370 °F
Zone 4
188 °C
370 °F
Zone 1
188 °C
370 °F
Zone 2
188 °C
370 °F
Zone 5
Melt Temperature 180 - 210 °C
356 - 410 °F
Mold Temperature 30.0 - 70.0 °C
86.0 - 158 °F
Roll Temperature 30.0 °C
86.0 °F
3rd Roll
40.0 °C
104 °F
2nd Roll
50.0 °C
122 °F
1st Roll
Drying Temperature <= 70.0 °C

@Time 10800 - 14400 sec
<= 158 °F

@Time 3.00 - 4.00 hour
Pre-drying in a dehumidifier
Moisture Content <= 0.15 %
<= 0.15 %
When Produced
Injection Pressure 75.2 - 120 MPa
10900 - 17400 psi
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions
Descriptive Properties Value Comments
Appearance Granule
Color Whitish
Injection Speed Moderate
Post Pressure, psi 5800 - 8700