Premix Thermoplastics PRE-ELEC® ABS 1415 Conductive Thermoplastic Compound

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Carbon Black Filled
Manufacturer Premix Thermoplastics Inc.
Trade Name PRE-ELEC®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® ABS 1415 Conductive Thermoplastic Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC® ABS 1415 is a conductive thermoplastic compound based on ABS. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® ABS 1415 has excellent mechanical properties and is easy to extrude.Applications: Extrusion of multi-layer sheet with natural HIPS, ABS or conductive or natural TPE.Processing PRE-ELEC® ABS 1415 compound can be processed in the machines using normal processing conditions as with ABS.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
Physical Properties Metric English Comments
Density 1.10 g/cc
0.0397 lb/in³
Thickness 102 microns
4.00 mil
Linear Mold Shrinkage 0.0050 - 0.0080 cm/cm
0.0050 - 0.0080 in/in
ISO 294-4
Melt Flow 2.5 g/10 min

@Load 10.0 kg,
Temperature 220 °C
2.5 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 77
77
ISO 868
Film Tensile Strength at Yield, MD 40.0 MPa

@Thickness 0.400 mm
5800 psi

@Thickness 0.0157 in
ISO 527
Film Elongation at Break, MD 10 %

@Thickness 0.400 mm
10 %

@Thickness 0.0157 in
ISO 527
Film Elongation at Break, TD 6.0 %

@Thickness 0.400 mm
6.0 %

@Thickness 0.0157 in
ISO 527
Film Elongation at Yield, MD 4.0 %

@Thickness 0.400 mm
4.0 %

@Thickness 0.0157 in
ISO 527
Flexural Modulus 1.90 GPa
276 ksi
ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Thickness 4.00 mm,
Temperature -20.0 °C
3.81 ft-lb/in²

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
15.0 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
7.14 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched (ISO) 60.0 kJ/m²

@Thickness 4.00 mm,
Temperature -20.0 °C
28.6 ft-lb/in²

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
NB

@Thickness 4.00 mm,
Temperature 23.0 °C
NB

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched NB

@Thickness 102 mm,
Temperature 23.0 °C
NB

@Thickness 4.00 in,
Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 1.50 J/cm²

@Thickness 102 mm,
Temperature -20.0 °C
7.14 ft-lb/in²

@Thickness 4.00 in,
Temperature -4.00 °F
ISO 179
1.70 J/cm²

@Thickness 102 mm,
Temperature 23.0 °C
8.09 ft-lb/in²

@Thickness 4.00 in,
Temperature 73.4 °F
ISO 179
Film Tensile Strength at Break, MD 22.0 MPa

@Thickness 0.400 mm
3190 psi

@Thickness 0.0157 in
ISO 527
Film Tensile Strength at Break, TD 22.0 MPa

@Thickness 0.400 mm
3190 psi

@Thickness 0.0157 in
ISO 527
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 88.0 °C
190 °F
75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi) 73.0 °C
163 °F
75/Method Af
Vicat Softening Point 91.0 °C
196 °F
ISO 306/B50
104 °C
219 °F
ISO 306/A50
Electrical Properties Metric English Comments
Volume Resistivity <= 1.00e+6 ohm-cm
<= 1.00e+6 ohm-cm
ISO D-257
Surface Resistance <= 1.00e+6 ohm
<= 1.00e+6 ohm
ISO IEC 61340-5-1
Processing Properties Metric English Comments
Zone 1 200 °C
392 °F
Cylinder
240 °C
464 °F
Die
Zone 2 210 °C
410 °F
Cylinder
230 °C
446 °F
Die
Zone 3 220 °C
428 °F
Die
220 °C
428 °F
Cylinder
Zone 4 230 °C
446 °F
Die
230 °C
446 °F
Cylinder
Zone 5 240 °C
464 °F
Die
240 °C
464 °F
Cylinder
Roll Temperature 60.0 °C
140 °F
3rd Roll
80.0 °C
176 °F
2nd Roll
90.0 °C
194 °F
1st Roll
Drying Temperature 80.0 - 100 °C
176 - 212 °F
Pre-drying
Dry Time 2 - 4 hour
2 - 4 hour
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions