Premix Premi-Glas® 3404 33% Glass Reinforced SMC

Category Polymer , Thermoset , Composite SMC , Filled/Reinforced Thermoset , Polyester, TS , Thermoset Polyester Glass SMC
Manufacturer Premix
Trade Name Premi-Glas®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Premi-Glas® 3404 33% Glass Reinforced SMC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Premi-Glas® 3404 is a glass reinforced thermoset sheet molding compound designed for mass transit and high strength flame retardant applications where low smoke and flame are required. Key features and benefits: Radiant panel flame spread index of less than 35 (ASTM E-162)Smoke Density less than 25 (ASTM E-662)In-mold powder color coating capableSpecially developed for low toxicity in rail and aircraft applicationsMarket: Mass TransitInformation provided by Premix.
Physical Properties Metric English Comments
Specific Gravity 1.83 g/cc
1.83 g/cc
Linear Mold Shrinkage 0.00030 cm/cm
0.00030 in/in
Polymerization Shrinkage
Mechanical Properties Metric English Comments
Tensile Strength 90.0 MPa
13100 psi
ASTM D638
Tensile Modulus 10.0 GPa
1450 ksi
ASTM D638
Flexural Strength 190 MPa
27600 psi
ASTM D790
Flexural Modulus 10.0 GPa
1450 ksi
ASTM D790
Poissons Ratio 0.30
0.30
Shear Modulus 3.80 GPa
551 ksi
Calculated
Izod Impact, Notched 5.50 J/cm
10.3 ft-lb/in
ASTM D256
Izod Impact, Unnotched 9.50 J/cm
17.8 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 35.0 µm/m-°C
19.4 µin/in-°F
Z Direction
CTE, linear, Transverse to Flow 25.0 µm/m-°C
13.9 µin/in-°F
XY Direction
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
Processing Properties Metric English Comments
Processing Temperature 150 °C
302 °F
Compression Molding
Clamp Pressure 3.45 - 6.89 MPa
500 - 1000 psi
Molding Pressure