Premix Premi-Glas® 1200H-15 Polyester SMC

Category Polymer , Thermoset , Composite SMC , Polyester, TS , Thermoset Polyester Glass SMC
Manufacturer Premix
Trade Name Premi-Glas®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Premi-Glas® 1200H-15 Polyester SMC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Premi-Glas® 1200H-15 is a 15% fiberglass-reinforced, thermoset, Sheet Molding Compound designed for applications where good arc resistance and dielectric strength are required and UL 94 HB flame recognition is sufficient. Key features and benefits are:Underwriters Laboratory UL 94HB flame recognition at 1.47mm minimum wall thickness. U.L flame recognized in all colors. Excellent flexural strength and flexural modulus properties. Designed for compression molding in matched metal molds. Available in fiberglass content of 10-30%.The Premi-Glas 1200-H series carries U.L 746 C recognition for use in exterior applications following ultraviolet light, water emersion and exposure testing.Data provided by Premix.
Physical Properties Metric English Comments
Specific Gravity 1.70 - 1.85 g/cc
1.70 - 1.85 g/cc
Linear Mold Shrinkage 0.0015 - 0.0025 cm/cm
0.0015 - 0.0025 in/in
Polymerization Shrinkage
Mechanical Properties Metric English Comments
Tensile Strength 35.0 MPa
5080 psi
ASTM D638
Tensile Modulus 12.0 GPa
1740 ksi
ASTM D638
Flexural Strength 95.0 MPa
13800 psi
ASTM D790
Flexural Modulus 9.50 GPa
1380 ksi
ASTM D790
Compressive Strength 145 MPa
21000 psi
ASTM D695
Poissons Ratio 0.30
0.30
Shear Modulus 4.60 GPa
667 ksi
Calculated
Izod Impact, Notched 4.25 J/cm
7.96 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.00 J/cm
11.2 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 35.0 µm/m-°C
19.4 µin/in-°F
Z Direction
CTE, linear, Transverse to Flow 25.0 µm/m-°C
13.9 µin/in-°F
XY Direction
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
UL RTI, Electrical 130 °C
266 °F
UL 746C
UL RTI, Mechanical with Impact 130 °C
266 °F
UL 746C
UL RTI, Mechanical without Impact 130 °C
266 °F
UL 746C
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Dielectric Strength 15.0 kV/mm
381 kV/in
ASTM D149
Arc Resistance 180 sec
180 sec
ASTM D495
Processing Properties Metric English Comments
Processing Temperature 150 °C
302 °F
Compression Molding
Clamp Pressure 3.45 - 6.89 MPa
500 - 1000 psi
Molding Pressure