Premix Premi-Glas® 1100-25 Fiberglass Reinforced Thermoset BMC

Category Polymer , Thermoset , Filled/Reinforced Thermoset
Manufacturer Premix
Trade Name Premi-Glas®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Premi-Glas® 1100-25 Fiberglass Reinforced Thermoset BMC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Premi-Glas® 1100-15 is a fiberglass reinforced thermoset bulk molding compound for general purpose applications requiring thermal stability and stiffness.Key features and benefits are:Excellent stiffness to weight ratio, non-meltingGood dimensional stability, including excellent thermal resistancePigmentable for molded-in color; best appearance with mold textureExcellent property retention in cold and hot environmentsGood corrosion resistance except in acid environments.Designed for compression or injection molding in matched metal die molds.Information provided by Premix.
Physical Properties Metric English Comments
Specific Gravity 1.70 - 1.85 g/cc
1.70 - 1.85 g/cc
Linear Mold Shrinkage 0.0015 - 0.0035 cm/cm
0.0015 - 0.0035 in/in
Polymerization Shrinkage
Mechanical Properties Metric English Comments
Tensile Strength 31.0 MPa
4500 psi
ASTM D638
Tensile Modulus 14.0 GPa
2030 ksi
ASTM D638
Flexural Strength 124 MPa
18000 psi
ASTM D790
Flexural Modulus 11.0 GPa
1600 ksi
ASTM D790
Poissons Ratio 0.30
0.30
Shear Modulus 5.40 GPa
783 ksi
Calculated
Izod Impact, Notched 4.25 J/cm
7.96 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.30 J/cm
9.93 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 35.0 µm/m-°C
19.4 µin/in-°F
Z Direction
CTE, linear, Transverse to Flow 24.0 µm/m-°C
13.3 µin/in-°F
XY Direction
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
Processing Properties Metric English Comments
Processing Temperature 150 °C
302 °F
Compression or Injection Molding
Clamp Pressure 3.45 - 6.89 MPa
500 - 1000 psi
Molding Pressure