Precision Polymer Engineering Z60B Hydrogenated NBR Compound

Category	Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE)
Manufacturer	Precision Polymer Engineering Limited
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Precision Polymer Engineering Z60B Hydrogenated NBR Compound.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Hydrogenated Nitrile Rubber, 55-65 °IRHD. Medium acrylonitrile (ACN) content. ASTM designation = HNBR. ASTM D2000 line call-out 2MDH614, A26, B36, EO16, EO36, F14.Applications: High strength and excellent chemical resistance. Higher operating temperature than standard nitrile. Suitable for use with sour (H2S) crude oil and gas, which may also include lubricating, oil additives and amine corrosion inhibitors. Good resistance to weathering and ozone.

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	60	60	°IRHD; ASTM D1415
	70	70	°IRHD, +10 change after 70 hours @ 150°C; ASTM D1415
Tensile Strength, Yield	10.5 MPa	1520 psi	-25% change after 70 hours @ 150°C; ASTM D412
	14.0 MPa	2030 psi	ASTM D412
Elongation at Break	175 %	175 %	-30% change after 70 hours @ 150°C; ASTM D412
	250 %	250 %	ASTM D412
Compression Set	50 %	50 %	24 hours @ 150°C; ASTM D395

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	180 °C	356 °F
Minimum Service Temperature, Air	-20.0 °C	-4.00 °F
	-18.0 °C	-0.400 °F	Non-brittle after 3 minutes
Flash Point	>= 300 °C	>= 572 °F