- Polyram RamOfin PPC301G2 Polypropylene, 10% Glass Fiber
Polyram RamOfin PPC301G2 Polypropylene, 10% Glass Fiber
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Glass Fiber Filler |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamOfin PPC301G2 Polypropylene, 10% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
10% glass fibers reinforced polypropylene copolymer for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in³ | DIN 53479 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM-D785 |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM-D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM-D638 |
| Flexural Strength | 50.0 MPa | 7250 psi | ASTM D790 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ASTM-D790 |
| Izod Impact, Notched | 1.70 J/cm @Temperature 23.0 °C |
3.18 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 °C | 329 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
Users viewing this material also viewed the following:
- Gharda Chemicals GATONE™ 5700 Polyetheretherketone (PEEK) (discontinued **)
- PTS Tristar® PC-10FRN (V) 15 MFI, 5VA, Flame Retardant, UV Stabilized Polycarbonate With Release
- Resinlab® CYNERGY CA6806 Adhesive
- Plaslok 506 Black Heat Resistant Mineral Filled Phenolic Molding Compound (discontinued **)
- SABIC Innovative Plastics Ultem 2412EPR PEI (Asia Pacific)
- Spartech PP7140 Talc Filled High Impact Copolymer
- SABIC Innovative Plastics Valox® V8090 PBT+PET (Europe-Africa-Middle East)
- Goodfellow Carbon-Carbon Composite
- Arlon CP-310R Bulk Compound
Copyright © lookpolymers.com All Rights Reserved